ASTM B338 Titanium Alloy Tube for Heat Exchangers with High Strength-to-Weight Ratio and Corrosion Resistance

Name: ASTM B338 Titanium Alloy Tube for Heat Exchangers with High Strength-to-Weight Ratio and Corrosion Resistance
Brand: Jiangsu Hongbao Group Co., Ltd.
SKU: HB-TI
Price: 22.00 USD
Availability: InStock

Detalhes do produto

Lugar de origem: Jiangsu, China

Marca: Hongbao

Certificação: DNV,PED,ISO,TUV,LR

Número do modelo: HB-TI

Termos de pagamento e envio

Quantidade de ordem mínima: 200kg

Preço: negotiable

Detalhes da embalagem: embalagem em caixa de madeira compensada em condições de navegar.

Tempo de entrega: NO PRAZO DE 50 DIAS

Termos de pagamento: L/C,D/A,D/P,T/T,Western Union

Habilidade da fonte: 800MT/ANO

Obtenha o melhor preço

Detalhes do produto

Descrição do produto

Destacar:

Material::	Gr1,Gr2,Gr3,Gr7,Gr9,Gr12	Certificado::	DNV,PED,ISO,TUV,LR
Grossura::	0.4-10mm	OD::	10-114MM
Comprimento::	100-15000 mm	Forma::	Redondo

Material::	Gr1,Gr2,Gr3,Gr7,Gr9,Gr12
Certificado::	DNV,PED,ISO,TUV,LR
Grossura::	0.4-10mm
OD::	10-114MM
Comprimento::	100-15000 mm
Forma::	Redondo

ASTM B338 Titanium Alloy Tube for Heat Exchangers with High Strength-to-Weight Ratio and Corrosion Resistance

For Heat Exchanger Pure Ti Titanium ASTM B338 GR2 GR7 GR9 Titanium Alloy Tubes

Optimize thermal efficiency with our premium titanium tubes, engineered for superior corrosion resistance and longevity in aggressive environments.

Key Features

Material Versatility: Choose the right grade for your needs:
- Gr2 (Pure Ti): The industry standard for excellent corrosion resistance and weldability
- Gr7 (Ti-Pd): Enhanced resistance against reducing acids and crevice corrosion
- Gr9 (Ti-3Al-2.5V): High strength-to-weight ratio, ideal for aerospace and high-pressure systems
Certified Quality: Fully compliant with ASTM B338, ensuring precise dimensions and metallurgical integrity
Superior Heat Transfer: Optimized wall thickness and smooth surface finish maximize thermal conductivity while minimizing fouling
Extreme Durability: Withstands seawater, chlorides, and oxidizing acids, guaranteeing a service life far beyond stainless steel

Applications

Shell & tube heat exchangers, condensers, marine coolers, chemical processing equipment, and power generation systems

Technical Specifications

Standard	ASTM B337, ASTM B338, ASTM B861, ASTM B862
Grade	Gr1, Gr2, Gr7, Gr9, Gr12
Dimension	ODWTL (10-114)(0.4-10)(100-15000)mm
Manufacturing Method	Cold rolled
Condition	Annealed (M)
Features	Light weight, excellent corrosion resistivity, strong heat-resistance, high strength
Inspection	Ultrasonic testing, Hydrostatic testing, Flattening testing, visual surface inspection, Dimensional inspection, tensile properties inspection and Chemical elements analysis

Basic Tension Data

Grade	Tensile Strength, min	Yield Strength 0.2% offset	Elongation in 2in or 50mm Min%
1	35 Ksi / 240 Mpa	20-45 Ksi / 138-310 Mpa	24
2	50 Ksi / 345 Mpa	40-65 Ksi / 275-450 Mpa	20
7	50 Ksi / 345 Mpa	40-65 Ksi / 275-450 Mpa	20
9A	125 Ksi / 860 Mpa	105 Ksi / 725 Mpa	10
9B	90 Ksi / 620 Mpa	70 Ksi / 483 Mpa	15
12	70 Ksi / 483 Mpa	50 Ksi / 345 Mpa	18

A. Properties for cold-worked and stress-relieved B. Annealed C. Solution treated

Chemical Composition of Material

Grade 1: Unalloyed titanium
Grade 2: Unalloyed titanium
Grade 7: Unalloyed titanium plus 0.12 to 0.25% palladium
Grade 9: Titanium alloy (3% aluminum, 2.35% vanadium)
Grade 12: Titanium alloy (0.3% molybdenum, 0.8% nickel)

Size Tolerance

Standard	OD Tolerance	WT Tolerance
ASTM B338	<25.4mm, ±0.102mm 24.4-38.1mm ±0.127mm 38.1-50.8mm ±0.152mm 50.8-63.5mm ±0.178mm 60.3-88.9mm ±0.254mm	±10%
ASTM B861	3.2-3.8mm -0.794/+0.397mm 38-102mm ±0.794mm 102-203mm 0.794/+1.588mm	±12.5%

Tags:

Tubo de aço soldado

tubo do aço da precisão

tubo de aço oco

Tubos de perfuração de petróleo

Tubo para Poço de Petróleo

Tubo sem emenda do titânio

Tubo Titanium da liga

tubo de aço sem emenda estirado a frio

Tubos de aço sem emenda da precisão

tubo recozido brilhante

Tubo do aço do rolamento

Tubo de aço de Bundy

Tubulação de aço automotivo

Tubo do permutador de calor

ASTM B338 Titanium Alloy Tube for Heat Exchangers with High Strength-to-Weight Ratio and Corrosion Resistance

tubulação fina da parede,

Tubo de ligas de aço,

tubulação redonda do metal

Tubo Titanium sem emenda Gr2 Gr3 da liga, tubulação fina da parede do diâmetro externo de 6mm

Resistência de erosão alta Titanium pura petroquímica ASTM do círculo de tubo B338

Escala exterior 6 - 219mm do diâmetro do tubo Titanium da liga Gr12 para a indústria química

Do recozimento brilhante do tubo dessanilização tóxica oca redonda não - resistente à corrosão

O tubo Titanium da liga do uso da aeronáutica conservou a espessura de parede grossa de 22mm

O tubo Titanium resistente ao calor da liga, pequeno diâmetro laminou o tubo 22mm OD

Redondo/quadrado soldou a tubulação Titanium a superfície conservada para o elemento do permutador de calor

Tubo Titanium da liga da propriedade criogênica, baixa tubulação da cavidade do módulo da elasticidade

padrão Titanium do tubo ASTM B861 da liga do comprimento de 5m para componentes da fuselagem

Tubo de titânio TC4 sem costura resistente à corrosão com alta resistência à tração e construção sem costura

Tubo de Liga de Titânio Gr9 Sem Emendas com Alta Relação Resistência-Peso e Resistência Superior à Corrosão

Tubo de aço soldado

tubo do aço da precisão

tubo de aço oco

Tubos de perfuração de petróleo

Tubo para Poço de Petróleo

Tubo sem emenda do titânio

Tubo Titanium da liga